Anti - corrosion High performance Top Coat for zinc aluminum flake AIA-1 manufacturer from China Changzhou Junhe Technology Stock Co.,Ltd

Anti - corrosion High performance Top Coat for zinc aluminum flake

Place of Origin:

Guangdong, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: AIA-1

1 General descript

1 General description

In view of the defect that dacromet coatings surface hardness is low, and no acid and alkali resistant,we learn from the advanced technology formulation,develop and produce JH-9323 dacromet coating, water-based dacromet coating,can not only increase the dacromet coatings surface hardness,acid and alkali resistance,and can improve the anti-corrosion performance of the coating (SST≥1500h).Have good adhesion with dacromet coating,and has many colors. Coating process is similar to dacromet coating,your first choice of dacromet top coat.

2 Perfomance charcteisic

This product is with acrylic acid copolymer resin, nitrocellulose, toughening agent and organic solvent as main base material, adding other additives mixed into.The coating layer is smooth, weak acid and alkali resistant, can be adjusted to any colour with paint.

3 Main Technical Data

No.	Item	Data	Test method
1	Appearance	Black,fine and smooth	Eye-measurement
2	Viscosity S≥	50	GB/T1723-93 second method
3	PH	8.0-9.0	PH-meter
4	Drying Time 140ºC/min	30	GB/T6751-86
5	Von-volatile% ≥	30	GB/T6751-86
6	Thickness of dry film (micron)	10-20	GB/T1764-79 (89) second method
7	Adhesion(degree)≤	1	GB/T9286-1998
8	Bend(mm)	1	GB/T1731-93
9	Hardness≥	1	GB/T1731-93
10	Impact resistance(kg•cm)	50	GB/T1732-93
11	heat and humidity resistance (h)	240	GB/T1740 70(80)
12	Gloss%≥	95	GB/T1743

4 Instructions and attention:

Dip coating,Spray coating etc.
It should be stirred fully befor usage; distilled water or deionized water can be used to adjust viscosity ;Operating viscosity:30-60s.