Technical Data Sheet

1   Product Information 

Trade Name: Zincover
Article/Model No.:JH-9382

2   Composition/information on ingredients

JH-9382 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic  additive. 
Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.
Pack C: It is the tackifier  of the coating which mainly made up of cellulose white or yellowish powder. 
 

3  Coating Process

3.1 Mix Ratio

Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if  spray coating)
Pack C:0-50 g (according to different viscosity demand )
3.2 
Before Mixture, Keep weighted A&B into the water bath at 25±2 , then stir A to make metal slurry disperse  uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add  B.
3.3  
Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35, startup refrigerating device to keep the barrel temperature constant at 35.
3.4 
Stir the mixture about 1~2 hours fast after B added, then add C.  C should be powdered if lump exist.(The barrel temperature should not be lower than 30, otherwise  C will not be dissolved sufficiently .)Then stir 12 hours continuously.
3.5
The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.
v
3.6
Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

5   Technical data

6  Mix Diagram

Caution: Temperature should be controlled in above operation.

7   Coating Process

7.1  Degreasing

The workpiece should be degreased if there is oil on the surface. There are three processing methods:
1.High temperature
2.Neutral water-base degreasing agent
3.Organic solvent such as methylene chloride.

7.2   Derusting

The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.

7.3   Coating

The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.

7.4   Pre-heating

The workpiece after coated should be Pre-heated as soon as possible at 80~150 for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)

7.5   Curing

The workpiece after pre-heating should be cured at  310-350 for 20-40mins. ( according to heat absorption of workpiece.)

8    Attentions

Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.
Avoid irradiation of sunshine and ultraviolet ray  for long time when operating, otherwise it will accelerate aging or polymerization of the coating .
It is very important to control the