Technical Data Sheet

Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

Film is silver white, the surface finish is good, high corrosion resistance, and then coated with good, anti scratch ability, salt spray performance than the national standard, the product liquid anti aging cycle longer, the same process conditions, the greater the amount of processing

1   Product Information 
Trade Name: Zincover
Article/Model No.:JH-9390

2   Composition/information on ingredients

JH-9390 is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and ethylene glycol. The radius-thickness ratio of Zn plate is 60~100.
Pack B: It is the solvent of the coating colored in orange-red and in water solution, which contain the  Cr6+.
Pack C: It is the tackifier  of the coating which mainly made up of cellulose white or yellowish powder. 

3  Coating Process

3.1 Mix Ratio
Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if  spray coating)
Pack C:0-50 g (according to different viscosity demand )
3.2 
Mixture Method
Before Mixture, Keep weighted A&B into the water bath at 25±2 , then stir A to make metal slurry disperse  uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add  B.
3.2.2
Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35, startup refrigerating device to keep the barrel temperature constant at 35.

3.2.3
Stir the mixture about 1~2 hours fast after B added, then add C.  C should be powdered if lump exist.(The barrel temperature should not be lower than 30, otherwise  C will not be dissolved sufficiently .)Then stir 12 hours continuously.
3.2.4
The coating should be filtrated by 80~100 mesh stainless steel screen before pouring into dip barrel.
3.2.5
Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.
3.2.6
Test density,PH,Temperature,Viscosity and Cr6+ content of coating every 8 hours if operate continuously.

5   Technical data

6  Mix Diagram

Caution: Temperature should be controlled in above operation.

7   Coating Process

7.1  Degreasing
The workpiece should be degreased if there is oil on the surface. There are three processing methods:
1.High temperature
2.Neutral water-base degreasing agent
3.Organic solvent such as methylene chloride.

7.2   Derusting
The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.

7.3   Coating
The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.

7.4   Pre-heating
The workpiece after coated should be Pre-heated as soon as possible at 80~150 for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)

7.5   Curing
The workpiece after pre-heating should be cured at  300-340 for 20-40 mins. ( according to heat absorption of workpiece.)

8    Attentions

Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.
Avoid irradiation of sunshine and ultraviolet ray  for long time when operating, otherwise it will accelerate aging or polymerization of the